Diyala University
  • Register
  • Login
  • العربیة

DIYALA JOURNAL OF ENGINEERING SCIENCES

  • Home
  • Browse
    • Current Issue
    • By Issue
    • By Subject
    • Keyword Index
    • Author Index
    • Indexing Databases XML
  • Journal Info
    • About Journal
    • Aims and Scope
    • Editorial Board
    • News
  • Guide for Authors
  • Submit Manuscript
  • Contact Us
Advanced Search

Notice

As part of Open Journals’ initiatives, we create website for scholarly open access journals. If you are responsible for this journal and would like to know more about how to use the editorial system, please visit our website at https://ejournalplus.com or
send us an email to info@ejournalplus.com

We will contact you soon

  1. Home
  2. Volume 10, Issue 4
  3. Author

ISSN: 1999-8716

Volume10, Issue4

EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE

    Hashim Shukur Hammood

DIYALA JOURNAL OF ENGINEERING SCIENCES, 2017, Volume 10, Issue 4, Pages 33-41

  • Show Article
  • Download
  • Cite
  • Statistics
  • Share

Abstract

This research studied the effect of the Heat Treatment on the Mechanical Properties and the Wear Rate of the pure Aluminum with a particle size of (≤53μm). The Aluminum is reinforced by graphite with a particle size of (≤63μm) with an addition of glass particles with different weight ratios of (3, 6, 9, and 12) Wt. % and a particle size was (≤ 53μm).
Powder metallurgy technique has been used to manufactured the samples, where the samples are pressed uniaxial at room temperature with (500 Map), then sintering at (550 C0) for (2 hr.). After that, heat treatment is applied on the samples at (500 OC) for one hour and Quenched in water.
There was a great improvement of the mechanical properties such as the hardens and the compressive strength. This improvement was proportional with the Weight ratio of the glass particles before and after the Heat Treatment.
On the other hand, there was a decrease of the wear rate versus the increase of the Weight ratio of the glass particles and heat treatment.
.
Keywords:
    powder metallurgy heat treatment wear rate compressive strength glass particles
  • PDF
  • XML
(2017). EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE. DIYALA JOURNAL OF ENGINEERING SCIENCES, 10(4), 33-41.
Hashim Shukur Hammood . "EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE". DIYALA JOURNAL OF ENGINEERING SCIENCES, 10, 4, 2017, 33-41.
(2017). 'EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE', DIYALA JOURNAL OF ENGINEERING SCIENCES, 10(4), pp. 33-41.
EFFECT OF GLASS ADDITION AND HEAT TREATMENT ON MECHANICAL PROPERTIES AND WEAR RATE OF ALUMINUM - 2% GRAPHITE. DIYALA JOURNAL OF ENGINEERING SCIENCES, 2017; 10(4): 33-41.
  • RIS
  • EndNote
  • BibTeX
  • APA
  • MLA
  • Harvard
  • Vancouver
  • Article View: 123
  • PDF Download: 95
  • LinkedIn
  • Twitter
  • Facebook
  • Google
  • Telegram
Journal Information

Publisher: Diyala University

Email:  engineering_college@diyengineering.net

Editor-in-chief: Dr. Amer Mohammed Ibrahim

  • Home
  • Glossary
  • News
  • Aims and Scope
  • Privacy Policy
  • Sitemap
This journal is licensed under a Creative Commons Attribution 4.0 International (CC-BY 4.0)

Powered by eJournalPlus